Nickel 201
Nickel 201

Nickel 201 alloy equal material :N02201, 2.4061,W.Nr 2.4060

Nickel 201 alloy as part of the malleability of industrial pure nickel. Pure nickel has good mechanical properties can be excellent corrosion resistant performance. Pure nickel has good chemical and magnetic properties.

Nickel 201 alloy Chemical composition:

Alloy

%

Ni

Fe

C

Mn

Si

Cu

S

Nickel 201

Min

Margin

 
 
 
 
 
 

Max

0.4

0.02

0.35

0.35

0.25

0.01

Nickel 201 alloy Physical properties:
Nickel 201 alloy density:8.89 g/cm³
Nickel 201 alloy Melting point:1440 degree

Nickel 201 alloy mechanical properties at room temperature, the minimum value :

State

Condition

Tensile strength Rm N/mm2

Yield strength

RP 0.2 N/mm2

Elongation

A5 %

Hardness HB

Nickel 201 alloy round bar

Hot rolled

60-85

15-45

35-55

45-80

Nickel 201 alloy round bar

Cold drawn or annealing

55-75

15-30

40-55

45-70

Nickel 201 alloy plate

Annealing

55-80

15-40

40-60

45-75

Nickel 201 alloy Sheet

Annealing

55-75

15-30

40-55

70 max

Nickel 201 alloy Pipe

Seamless annealing

55-75

12-30

40-60

70 max

Nickel 201 Features:

Nickel200 is very low carbon content of the pure commercial nickel, has been approved for use in service is as high as 1230 degree high temperature environment.

Nickel 201 Application fields:
Food processing equipment, salt refining equipment.
Mining and ocean mining.
At above 300 degree under the condition of equipment needed for manufacturing industrial sodium hydroxide.
Organic or inorganic chloride and fluoride production: corrosion resistance to chlorine and fluorine
A nuclear reactor
Retort and parts heat treatment furnace, especially in the carbide and nitride atmosphere
Catalytic regenerator in petrochemical production is recommended to use in the application of above 700 degree alloy 600 to obtain a longer service life.

Related Link:Nickel 200,Nickel 201 ,Nickel alloys and super alloys