Inconel625 face-centered cubic lattice structure, organic process technology components containing chloride, for a variety of corrosive media oxidative and reductive environment has very good corrosion resistance.
Inconel 625 Chemical compositon
% |
Ni |
Cr |
Mo |
Fe |
Al |
Ti |
C |
Mn |
Si |
Cu |
P |
S |
Min |
58 |
20 |
8 |
|
|
|
|
|
|
|
|
|
Max |
|
23 |
10 |
5 |
0.4 |
0.4 |
0.1 |
0.5 |
0.5 |
0.5 |
0.015 |
0.015 |
Density |
8.4 g/cm3 |
Melting point |
1290-1350℃ |
Alloy |
Tensile strength Rm N/mm2 |
Yield Strength RP0.2N/mm2 |
Elongation A5 % |
Brinell hardness HB |
Inconel625 |
760 |
345 |
30 |
≤220 |
Inconel 625 Property :
1.A variety of corrosive media oxidative and reductive environment have very good corrosion resistance
2.Excellent resistance to corrosion and crevice corrosion points, and no cause due to chloride stress corrosion cracking
3.Excellent corrosion resistance to inorganic acids, such as nitric acid, phosphoric acid, sulfuric acid, hydrochloric acid and a mixed acid of sulfuric acid and hydrochloric acid, etc.
4.Excellent resistance to inorganic acid mixed solution capabilities corrosion
5.Temperature of 40 ℃, at various concentrations of hydrochloric acid solution can exhibit excellent corrosion resistance
6.Good workability and weldability, no weld cracking susceptibility
7.Having a wall temperature of -196 ~ 450 ℃ in a pressure vessel for manufacturing certification
8.By the American Association of Corrosion Engineers NACE standard certification (MR-01-75) meet the highest standards of grade VII of sour gas environments
Inconel 625 Metallurgical structure
625 for the face-centered cubic lattice structure. After incubation for sufficient time at about 650 ℃, the deposited carbon particles and unstable quaternary phase and into stable Ni3 (Nb, Ti) phase orthorhombic lattice. Nickel-chromium matrix molybdenum, niobium solid solution strengthening component will improve the mechanical properties of the material, but the plastic will be reduced.
Inconel 625 application
1.Organic Chemistry Process Technology of chloride-containing components, particularly in the case of using an acid chloride catalyst
2.For the manufacture of pulp and paper industry and bleaching digester tank
3.FGD absorber system, another heater flue gas inlet baffle, fan (wet), stirrer, baffle and flue
4.Applied to the acidic environment for the manufacture of gas equipment and components
5.Acetic acid and acetic anhydride generator
6.Sulfuric acid condenser