Nickel 201 alloy equal material :N02201, 2.4061,W.Nr 2.4060
Nickel 201 alloy as part of the malleability of industrial pure nickel. Pure nickel has good mechanical properties can be excellent corrosion resistant performance. Pure nickel has good chemical and magnetic properties.
| Alloy |
% |
Ni |
Fe |
C |
Mn |
Si |
Cu |
S |
|
Nickel 201 |
Min |
Margin |
|
|
|
|
|
|
|
Max |
0.4 |
0.02 |
0.35 |
0.35 |
0.25 |
0.01 |
Nickel 201 alloy Physical properties:
Nickel 201 alloy density:8.89 g/cm³
Nickel 201 alloy Melting point:1440 degree
Nickel 201 alloy mechanical properties at room temperature, the minimum value:
|
State |
Condition |
Tensile strength Rm N/mm2 |
Yield strength |
Elongation |
Hardness HB |
|
Nickel 201 alloy round bar |
Hot rolled |
60-85 |
15-45 |
35-55 |
45-80 |
|
Nickel 201 alloy round bar |
Cold drawn or annealing |
55-75 |
15-30 |
40-55 |
45-70 |
|
Nickel 201 alloy plate |
Annealing |
55-80 |
15-40 |
40-60 |
45-75 |
|
Nickel 201 alloy Sheet |
Annealing |
55-75 |
15-30 |
40-55 |
70 max |
|
Nickel 201 alloy Pipe |
Seamless annealing |
55-75 |
12-30 |
40-60 |
70 max |
Nickel 201 Features:
Nickel200 is very low carbon content of the pure commercial nickel, has been approved for use in service is as high as 1230 degree high temperature environment.
Nickel 201 Application fields:
Food processing equipment, salt refining equipment.
Mining and ocean mining.
At above 300 degree under the condition of equipment needed for manufacturing industrial sodium hydroxide.
Organic or inorganic chloride and fluoride production: corrosion resistance to chlorine and fluorine
A nuclear reactor
Retort and parts heat treatment furnace, especially in the carbide and nitride atmosphere
Catalytic regenerator in petrochemical production is recommended to use in the application of above 700 degree alloy 600 to obtain a longer service life.