W.Nr.2.4061 alloy equal material :N02201, 2.4061,W.Nr 2.4060
W.Nr.2.4061 alloy as part of the malleability of industrial pure nickel. Pure nickel has good mechanical properties can be excellent corrosion resistant performance. Pure nickel has good chemical and magnetic properties.
| Alloy |
% |
Ni |
Fe |
C |
Mn |
Si |
Cu |
S |
|
W.Nr.2.4061 |
Min |
Margin |
|
|
|
|
|
|
|
Max |
0.4 |
0.02 |
0.35 |
0.35 |
0.25 |
0.01 |
W.Nr.2.4061 alloy Physical properties:
W.Nr.2.4061 alloy density:8.89 g/cm³
W.Nr.2.4061 alloy Melting point:1440 degree
W.Nr.2.4061 alloy mechanical properties at room temperature, the minimum value :
| State |
Condition |
Tensile strength Rm N/mm2 |
Yield strength |
Elongation |
Hardness HB |
|
W.Nr.2.4061 alloy round bar |
Hot rolled |
60-85 |
15-45 |
35-55 |
45-80 |
|
W.Nr.2.4061 alloy round bar |
Cold drawn or annealing |
55-75 |
15-30 |
40-55 |
45-70 |
|
W.Nr.2.4061 alloy plate |
Annealing |
55-80 |
15-40 |
40-60 |
45-75 |
|
W.Nr.2.4061 alloy Sheet |
Annealing |
55-75 |
15-30 |
40-55 |
70 max |
|
W.Nr.2.4061 alloy Pipe |
Seamless annealing |
55-75 |
12-30 |
40-60 |
70 max |
W.Nr.2.4061 Features:
Nickel200 is very low carbon content of the pure commercial nickel, has been approved for use in service is as high as 1230 degree high temperature environment.
W.Nr.2.4061 Application fields:
Food processing equipment, salt refining equipment.
Mining and ocean mining.
At above 300 degree under the condition of equipment needed for manufacturing industrial sodium hydroxide.
Organic or inorganic chloride and fluoride production: corrosion resistance to chlorine and fluorine
A nuclear reactor
Retort and parts heat treatment furnace, especially in the carbide and nitride atmosphere
Catalytic regenerator in petrochemical production is recommended to use in the application of above 700 degree alloy 600 to obtain a longer service life.