+ZM means Hot-dip Zinc-magnesium alloy coated, application of a Zinc-magnesium coating by immersing the prepared strip in a molten bath of zinc-aluminum-magnesium. The composition of the bath is sum of aluminium and magnesium from 1.5%-8%, containing minimum of 0.2% magnesium and the balance zinc. So HCT450X+ZM means hot dip zinc-magnesium coated, dual-phase quality steel material for cold forming .
HCT450X+ZM material steel have coil, strip, sheet condition, thickness is from 0.2mm-3mm.
HCT450X+ZM steel coating finish is N(Normal spangle) or M(Minimized spangle)
HCT450X+ZM steel Surface quality A (As coated surface) , B(Improved surface), C(Best quality surface)
HCT450X+ZM steel Surface treatment C (chemically passivated) , O (oiled), CO (chemically passivated and oiled) , P (phosphate) , PO (phosphate and oiled), S (sealed)
HCT450X+ZM steel Coating mass are: ZF100, ZF120
HCT450X+ZM steel mechanical property:
Yield strength should be 260-340MPa
Tensile strength should be not less than 450MPa
Elongation A80 should be not less than 27%
Strain hardening exponent should be not less than 0.16
Bake hardening index BH2 should be mot than than 30MPa
Elongation A80 should be not less than 13%