ANSWER:HCT490X+ZF is a hot dip Zinc-iron coated steel grade in European standard EN10346 ,HCT490X+ZF is dual-phase quality steel material for cold forming (the steel consisting of mainly ferrite and martensite and possible bainite as a complementary phase ), The material No. of HCT490X+ZF is 1.0995+ZF.
+ZF means hot dip Zinc-iron coating. The zinc content of the bath is at least 99%, or the annealing produces and iron-zinc coating with an iron content of normally 8%-12%. So HCT490X+ZF means hot dip zinc-iron coated, dual-phase quality steel material for cold forming .
HCT490X+ZF material steel have coil, strip, sheet condition, thickness is from 0.2mm-3mm.
HCT490X+ZF steel coating finish is N(Normal spangle) or M(Minimized spangle)
HCT490X+ZF steel Surface quality A (As coated surface) , B(Improved surface), C(Best quality surface)
HCT490X+ZF steel Surface treatment C (chemically passivated) , O (oiled), CO (chemically passivated and oiled) , P (phosphate) , PO (phosphate and oiled), S (sealed)
HCT490X+ZF steel Coating mass are: ZF100, ZF120
Yield strength should be 290-380MPa
Tensile strength should be not less than 490MPa
Elongation A80 should be not less than 24%
Strain hardening exponent should be not less than 0.15
Bake hardening index BH2 should be mot than than 30MPa