What’s HX260BD+ZM steel ?

ASK:

What's HX260BD+ZM steel ?

ANSWER:HX260BD+ZM is a hot dip Zinc-iron coated steel grade in European standard EN10346 ,HX260BD+ZM is bake hardening quality steel material (the steel exhibiting an increase in proof strength following heating in the region of 170 °C for 20 min ), The material No. of HX260BD is 1.0924+ZM.

+ZM means Hot-dip Zinc-magnesium alloy coated, application of a Zinc-magnesium coating by immersing the prepared strip in a molten bath of zinc-aluminum-magnesium. The composition of the bath is sum of aluminium and magnesium from 1.5%-8%, containing minimum of 0.2% magnesium and the balance zinc. So HX260BD+ZM means hot dip Zinc-magnesium coated,cold forming quality material with bake hardening quality.

HX260BD+ZM material steel have coil, strip, sheet condition, thickness is from 0.2mm-3mm.

HX260BD+ZM steel coating finish is N(Normal spangle) or M(Minimized spangle)

HX260BD+ZM steel Surface quality A (As coated surface) , B(Improved surface), C(Best quality surface) HX260BD+ZM steel Surface treatment C (chemically passivated) , O (oiled), CO (chemically passivated and oiled) , P (phosphate) , PO (phosphate and oiled), S (sealed)

HX260BD+ZM steel Coating mass are: ZM060, ZM070, ZM080,ZM090,ZM100,ZM120, ZM130, ZM140, ZM150, ZM160, ZM175, ZM190, ZM200, ZM250, ZM300, ZM310, ZM350, ZM430,

HX260BD+ZM steel mechanical property:
Proof strength should be 260-320MPa
Tensile strength should be 360-440MPa
Elongation A80 should be not less than 28%
Bake-hardening Index BH2 should be not less than 30MPa