+ZF means hot dip Zinc-iron coating. The zinc content of the bath is at least 99%, or the annealing produces and iron-zinc coating with an iron content of normally 8%-12%. So HX300YD+ZF means hot dip zinc-iron coated, cold forming material steel with high proof strength .
HX300YD+ZF material steel have coil, strip, sheet condition, thickness is from 0.2mm-3mm.
HX300YD+ZF steel coating finish is N(Normal spangle) or M(Minimized spangle)
HX300YD+ZF steel Surface quality A (As coated surface) , B(Improved surface), C(Best quality surface)
HX300YD+ZF steel Surface treatment C (chemically passivated) , O (oiled), CO (chemically passivated and oiled) , P (phosphate) , PO (phosphate and oiled), S (sealed)
HX300YD+ZF steel Coating mass are: ZF100, ZF120
HX300YD+ZF steel mechanical property:
Proof strength should be 300-360MPa
Tensile strength should be 390-470MPa
Elongation A80 should be not less than 30%
Plastic strain ratio r90 should be not less than 1.3
Strain hardening exponent n90 should be not less than 0.15