ANSWER:HX340BD is a steel grade in European standard EN10346, HX340BD+ZM is bake hardening quality steel material (the steel exhibiting an increase in proof strength following heating in the region of 170 °C for 20 min ), The material No. of HX340BD is 1.0945.
+ZA means Hot-dip Zinc-aluminium alloy coated, application of a Zinc-aluminium coating by immersing the prepared strip in a molten bath of zinc-aluminum-aluminium. The composition of the bath is approximately 5% aluminum, small amounts of mischmetal and the balance zinc. So HX340BD+ZA means hot dip Zinc-aluminium coated, cold forming quality material with bake hardening quality.
HX340BD+ZA material steel have coil, strip, sheet condition, thickness is from 0.2mm-3mm.
HX340BD+ZA steel coating finish is N(Normal spangle) or M(Minimized spangle)
HX340BD+ZA steel Surface quality A (As coated surface) , B(Improved surface), C(Best quality surface)
HX340BD+ZA steel Surface treatment C (chemically passivated) , O (oiled), CO (chemically passivated and oiled) , P (phosphate) , PO (phosphate and oiled), S (sealed)
HX340BD+ZA steel Coating mass are: ZA095, ZA130, ZA185, ZA200, ZA255, ZA300
HX340BD+ZA steel mechanical property:
Proof strength should be 340-400MPa
Tensile strength should be 440-520MPa
Elongation A80 should be not less than 24%
Bake-hardening Index BH2 should be not less than 30MPa